Double-Component Hollow Glass Silicone Sealant, Non-Structural Seals
|FOB Price:||US $50-550 / Set|
|Min. Order:||20 Sets|
|Min. Order||FOB Price|
|20 Sets||US $50-550/ Set|
|Transport Package:||a, 200L/Bucket; B, 20L/Bucket|
|Payment Terms:||L/C, T/T, D/P, Western Union, Paypal, Money Gram|
- Model NO.: XGM-525
- Morphology: Water Emulsion
- Material: Silicone
- Main Agent Composition: Natural Polymer
- Promoter Composition: Curing Agent
- Color: White and Black
- Specification: A, 200L/Bucket; B, 20L/Bucket
- Bonding Function: High Temperature Resistant Adhesive
- Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
- Classification: Room Curing
- Characteristic: Adhesive Seals of Non-Structural Hollow Glass
- Composition: Organic Material
- Trademark: XINGUANGMING
- Origin: Sichuang, China
Features : 1 , two-component , the curing velocity could be adjusts , and can be uses as any factory's construct .
2 , neutral curing , with great cohesiveness for any kinds of glass and aluminum products .
3 , excellent mechanical property .
4 , with great climate aging resistance performance , and high/low temperature resistance .
Color : white , black , will be black after mix .
Executive standard : GB/T 29755-2013<<HOLLOW GLASS ELASTIC SEALANT>>
Packaging details: part A) 200L/Bucket(Net content 180L) ,part B)20L/bucket (Net content 28kg) .
Storage condition: Airtight store in a cool ventilated dry place , under normal temperature . Storage life is 12 months from date of manufacture .
Mix proportion : A volume ratio 9:1 ~ 11:1 , B mass ratio 11:1 ~ 13:1 .
Announcements: must keep the building drying, cleaning and no-oil before use it .
Can not use it in a place of wet all the year round and permeate oil out .
can not be use if the material surface temperature is under 4ºC or exceed 40ºC ,
can not be uses on frosty or moist surface .
This product will not be with toxic after curing , but please avoid it contact with your eyes before it cures , please watch out your children , do not touch non-curing products .
Curing time : this product will gets gel reaction all , if part A and B mixed . It will not be influenced by outside humidity , the surface drying time is concerned with mix proportion of part A and B .
|Project||Technical index||Test result|
|Fine and smooth, viscous body, no bubble and skinning, every part's color is not same||Part B has permeate oil out. the colors are difference obviously|
|2||Density , g/cm3||Part A||1.4±0.1||1.5|
|3||Sag||Vertical , mm||≤3||2.8|
|4||Probation period , min||≥20||61|
|5||Surface drying time , h||≤2||1.2|
|6||Hardness , ShoreA||30 ~ 60||51|
|7||Tensile adhesive strength, MPa||≥0.60||0.85|
|Tensile elongation of maximum strength,||≥50||101|
|Adhesive damage area , %||≤10||0|
|8||Tensile properties at maintained extension||Non-damaging||Non-damaging|