Double Component Silicone Structural Sealant, Glass Curtain Wall.
|FOB Price:||US $75-800 / Set|
|Min. Order:||20 Sets|
|Min. Order||FOB Price|
|20 Sets||US $75-800/ Set|
|Payment Terms:||L/C, T/T, D/P, Western Union, Paypal, Money Gram|
- Model NO.: XGM-909
- Morphology: Water Emulsion
- Material: Silicone
- Main Agent Composition: Natural Polymer
- Promoter Composition: Curing Agent
- Color: White , Black , and Mixed
- Transport Package: a, 200L/Bucket; B, 20L/Bucket
- Origin: Sichuang, China
- Bonding Function: Structural Adhesive
- Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
- Classification: Room Curing
- Characteristic: Weatherability
- Composition: Organic Material
- Trademark: XINGUANGMING
- Specification: A, 200L/Bucket; B, 20L/Bucket
2 , adhesive seals of hollow glass in second structure .
3 , other correlation building's structures .
Features : 1 , two-component , neutral curing , the curing velocity could be adjusts , and be the same with any factory's construct .
2 , excellent mechanical property .
3 , non-corrosiveness with multifarious glass materials such as coated glass , tempered glass , LOW-E glass , laminated glass , etc .
4 , with great climate aging resistance .
Color : part A is white , B is black , and it will be black too after mix .
Executive standard : GB/T 29755-2013<<HOLLOW GLASS ELASTIC SEALANT>>
Packaging details: part A) 200L/Bucket (Net content 190L),part B)20L/bucket (Net content 28kg) .
Storage condition: Airtight store in a cool ventilated dry place , under normal temperature . Storage life is 12 months from date of manufacture .
Mix proportion : A volume ratio 9:1 ~ 11:1 , B mass ratio 11:1 ~ 13:1 .
Announcements: must keep the building drying, cleaning and no-oil before use it .
Can not use it in a place of wet all the year round and permeate oil out .
can not be use if the material surface temperature is under 4ºC or exceed 40ºC ,
can not be uses on frosty or moist surface .
Curing time : this product will gets gel reaction all , if part A and B mixed . It will not be influenced by outside humidity , the surface drying time is concerned with mix proportion of part A and B .
|Project||Technical index||Test result|
|Fine and smooth, viscous body, no bubble and skinning, every part's color is not same||Fine and smooth without bubble and skinning , the colors are difference obviously|
|2||Density , g/cm3||Part A||1.4±0.1||1.4|
|3||Sag||Vertical , mm||≤3||1.2|
|4||Probation period , min||≥20||52|
|5||Surface drying time , h||≤2||1.0|
|6||Hardness , ShoreA||30 ~ 60||46|
|7||Tensile adhesive strength, MPa||≥0.60||0.98|
|Tensile elongation of maximum strength,||≥50||120|
|Adhesive damage area , %||≤10||0|
|8||Tensile properties at maintained extension||Non-damaging||Non-damaging|